Traditional Corrosion Tests arşivleri

1.1.1 TS EN ISO 9227 / ASTM B117

Neutral Salt Spray Resistance Test Test samples are continuously sprayed with 5% concentration saltwater onto the test specimen inside a chamber at 35 ± 2°C for the specified test duration. At the end of the test, organic coated parts are evaluated and interpreted according to the following standards: TS EN ISO 4628-2 / ASTM D714 […]

1.1.2 TS EN ISO 9227 / ASTM G85

Acetic Acid Salt Spray Resistance Test Test samples are continuously sprayed with a saltwater solution at 5% concentration, adjusted with acetic acid to a pH range of 3.1 – 3.3, onto the test specimen inside a chamber at 35 ± 2°C for the specified test duration. At the end of the test, the evaluation is […]

1.1.3 TS EN ISO 9227 / ASTM B368

Copper-Accelerated Acetic Acid Salt Spray Resistance Test The purpose of the test is to examine the effects that may be observed on the surface when the sample is exposed to polluted atmospheres. Test samples are placed in a chamber at 50 ± 2°C, where a 5% concentration saltwater solution is prepared by adding copper(II) chloride […]

1.1.4 TS EN ISO 6270-1

Determination of Moisture Resistance – Continuous Molding This test is preferred to determine the resistance of paint films, coating systems, and related products to high humidity conditions according to the requirements specified in the coating or product specifications. This method can be applied to coatings on both porous substrate materials, such as wood, plaster, and […]

1.1.5 TS EN ISO 6270-2 / ASTM D2247

Determination of Moisture Resistance – Exposure to Condensation in a Water Environment Method This method covers the determination of the resistance of paint films, coating systems, and related products to high humidity conditions, as specified in the coating or product specifications. This method can be applied to coatings on both porous substrates, such as wood, […]

1.1.6 TS EN ISO 22479

Resistance Test to Sulfur Dioxide Containing Humid Atmospheres Sulfur dioxide is a pollutant gas that can be found in industrial areas and certain atmospheric conditions. Sulfur dioxide can cause acidic corrosion in materials. This test is preferred to determine the material and coating's resistance to acidic and corrosive environmental conditions.

1.1.7 TS EN ISO 12944-6

Corrosion Protection of Steel Structures Coated with Protective Paint Systems ISO 12944-6 standard is an international standard that provides a comprehensive approach to the protection of steel structures using protective paint systems. The main objective of this standard is to identify and classify suitable paint systems to effectively protect steel structures against corrosion in various […]

1.1.8 TS EN ISO 2812-1/2/3/4

Determination of Liquid Resistance The EN ISO 2812 standard aims to measure the resistance of coating systems to various chemical substances. The purpose of this standard is to determine and evaluate the performance of paints and varnish coatings against chemical influences. TS EN ISO 2812 tests the chemical resistance of coatings by exposing them to […]

Traditional Corrosion Tests

1.1.1 TS EN ISO 9227 / ASTM B117

1.1.2 TS EN ISO 9227 / ASTM G85

1.1.3 TS EN ISO 9227 / ASTM B368

1.1.4 TS EN ISO 6270-1

1.1.5 TS EN ISO 6270-2 / ASTM D2247

1.1.6 TS EN ISO 22479

1.1.7 TS EN ISO 12944-6

1.1.8 TS EN ISO 2812-1/2/3/4